Characteristics of tin-containing fluoride toothpastes related to erosive tooth wear protection.
Publisher DOI
PubMed ID
38417610
Abstract
OBJECTIVES
To assess the effect of different tin-containing toothpastes on the control of erosive tooth wear in enamel and dentin.
METHODS
Enamel and dentin slabs were randomly distributed into 7 experimental groups (n=10/substrate): C-: negative control (Artificial saliva); AmF (regular fluoridated toothpaste without tin); Sn-1 (SnF2/NaF); Sn-2 (SnF2/NaF/SnCl2); Sn-3 (SnCl2/NaF); Sn-4 (SnF2/SnCl2); Sn-5 (SnCl2/AmF/NaF/chitosan). Specimens were submitted to 5-day erosion-abrasion cycling. Surface loss (SL) was determined with an optical profilometer. Tin deposition on the tooth surfaces and some characteristics of the toothpastes (pH, potentially available F-, %weight of solid particles, and RDA) were also assessed. Data were statistically analyzed (α=0.05).
RESULTS
For enamel, the Sn-2 presented the lowest SL, not differing significantly from AmF, C+, and Sn-3. The SL of these groups was significantly lower than the C-, except for Sn-3. Sn-1 and Sn-4 were also not significantly different from C-. For dentin, C- significantly showed the highest SL values, whilst, Sn-1 presented the lowest SL, not differing significantly from AmF, Sn-2, C+, and Sn-3. There was a significant positive association between enamel SL and the pH and tin deposition. Dentin SL was significantly negatively associated with the %weight of solid particles and RDA.
CONCLUSIONS
Most of the tin-toothpastes were able to exhibit some protection against ETW. In this process, the toothpastes characteristics play a role, as lower enamel SL was significantly associated with lower pH values and tin deposition; and lower dentin SL was associated with higher %weight of solid particles and RDA of the toothpastes.
To assess the effect of different tin-containing toothpastes on the control of erosive tooth wear in enamel and dentin.
METHODS
Enamel and dentin slabs were randomly distributed into 7 experimental groups (n=10/substrate): C-: negative control (Artificial saliva); AmF (regular fluoridated toothpaste without tin); Sn-1 (SnF2/NaF); Sn-2 (SnF2/NaF/SnCl2); Sn-3 (SnCl2/NaF); Sn-4 (SnF2/SnCl2); Sn-5 (SnCl2/AmF/NaF/chitosan). Specimens were submitted to 5-day erosion-abrasion cycling. Surface loss (SL) was determined with an optical profilometer. Tin deposition on the tooth surfaces and some characteristics of the toothpastes (pH, potentially available F-, %weight of solid particles, and RDA) were also assessed. Data were statistically analyzed (α=0.05).
RESULTS
For enamel, the Sn-2 presented the lowest SL, not differing significantly from AmF, C+, and Sn-3. The SL of these groups was significantly lower than the C-, except for Sn-3. Sn-1 and Sn-4 were also not significantly different from C-. For dentin, C- significantly showed the highest SL values, whilst, Sn-1 presented the lowest SL, not differing significantly from AmF, Sn-2, C+, and Sn-3. There was a significant positive association between enamel SL and the pH and tin deposition. Dentin SL was significantly negatively associated with the %weight of solid particles and RDA.
CONCLUSIONS
Most of the tin-toothpastes were able to exhibit some protection against ETW. In this process, the toothpastes characteristics play a role, as lower enamel SL was significantly associated with lower pH values and tin deposition; and lower dentin SL was associated with higher %weight of solid particles and RDA of the toothpastes.
Date Issued
2024-04
Publication Type
Article
Subject(s)
Subjects
Erosive tooth wear dental erosion fluoride tin tooth abrasion toothpaste
Language(s)
en
Author(s)
Sakae, Letícia Oba | |
Kairalla, Cláudia Allegrini | |
Viana, Ítallo Emídio Lira | |
Hara, Anderson Takeo | |
Scaramucci, Taís |
Journal
Journal of dentistry
Publisher
Elsevier
ISSN
1879-176X
Access(Rights)
restricted