Surface roughness of dental implants and treatment time using six different implantoplasty procedures.
Publisher DOI
PubMed ID
26355907
Abstract
OBJECTIVES
To test whether or not one of six implantoplasty procedures is superior to the others rendering a minimal final implant surface roughness and a short treatment time.
MATERIAL AND METHODS
Forty-two one-piece implants were embedded in epoxy resin blocks with 6-mm rough implant surface exposed. The following implantoplasty polishing sequences were applied: Brownie(®) , Greenie(®) sequence (BG) (diamond rotary instruments 106-, 40-, 15-μm grit, Brownie(®) , Greenie(®) silicone polishers); Arkansas stone sequence (AS) (diamond 106-, 40-, 15-μm grit, Arkansas stone torpedo-shaped bur); Short diamond sequence (SD) (diamond 106-, 40-, 4-μm grit); Short diamond sequence with Greenie(®) (SDG) (diamond 106-, 40-, 4-μm grit, Greenie(®) ); Complete diamond sequence (CD) (diamond 106-, 40-, 15-, 8-, 4-μm grit); Complete diamond sequence with Greenie(®) (CDG) (106-, 40-, 15-, 8-, 4-μm grit, Greenie(®) ). The polished neck portion served as a positive control, the untreated sandblasted and acid-etched surface as negative control. Each implant was scanned with a contact profilometer rendering Ra values and Rz values as a measure of surface roughness. The time needed to polish the implant surface for each group was recorded. Simultaneous comparisons between more than two groups were done performing Kruskal-Wallis tests. Comparisons between two groups were analysed using Wilcoxon rank-sum tests.
RESULTS
Mean Ra values amounted to 0.32 ± 0.14 μm (BG), 0.39 ± 0.13 μm (AS), 0.59 ± 0.19 μm (SDG), 0.71 ± 0.22 μm (SD), 0.75 ± 0.26 μm (CDG), 0.98 ± 0.30 μm (CD), 0.10 ± 0.01 μm (PC) and 1.94 ± 0.47 μm (NC). Pairwise one-sided comparisons between the test group revealed statistically significant differences (P < 0.05). The shortest treatment time was recorded for group AS (13 ± 2 min) and the longest for CDG (21 ± 2 min) and BG (21 ± 4 min).
CONCLUSIONS
Considering final surface roughness and treatment duration, the use of rotary diamond burs in decreasing roughness, followed by an arkansas stone (group AS), appears to be an optimal treatment option.
To test whether or not one of six implantoplasty procedures is superior to the others rendering a minimal final implant surface roughness and a short treatment time.
MATERIAL AND METHODS
Forty-two one-piece implants were embedded in epoxy resin blocks with 6-mm rough implant surface exposed. The following implantoplasty polishing sequences were applied: Brownie(®) , Greenie(®) sequence (BG) (diamond rotary instruments 106-, 40-, 15-μm grit, Brownie(®) , Greenie(®) silicone polishers); Arkansas stone sequence (AS) (diamond 106-, 40-, 15-μm grit, Arkansas stone torpedo-shaped bur); Short diamond sequence (SD) (diamond 106-, 40-, 4-μm grit); Short diamond sequence with Greenie(®) (SDG) (diamond 106-, 40-, 4-μm grit, Greenie(®) ); Complete diamond sequence (CD) (diamond 106-, 40-, 15-, 8-, 4-μm grit); Complete diamond sequence with Greenie(®) (CDG) (106-, 40-, 15-, 8-, 4-μm grit, Greenie(®) ). The polished neck portion served as a positive control, the untreated sandblasted and acid-etched surface as negative control. Each implant was scanned with a contact profilometer rendering Ra values and Rz values as a measure of surface roughness. The time needed to polish the implant surface for each group was recorded. Simultaneous comparisons between more than two groups were done performing Kruskal-Wallis tests. Comparisons between two groups were analysed using Wilcoxon rank-sum tests.
RESULTS
Mean Ra values amounted to 0.32 ± 0.14 μm (BG), 0.39 ± 0.13 μm (AS), 0.59 ± 0.19 μm (SDG), 0.71 ± 0.22 μm (SD), 0.75 ± 0.26 μm (CDG), 0.98 ± 0.30 μm (CD), 0.10 ± 0.01 μm (PC) and 1.94 ± 0.47 μm (NC). Pairwise one-sided comparisons between the test group revealed statistically significant differences (P < 0.05). The shortest treatment time was recorded for group AS (13 ± 2 min) and the longest for CDG (21 ± 2 min) and BG (21 ± 4 min).
CONCLUSIONS
Considering final surface roughness and treatment duration, the use of rotary diamond burs in decreasing roughness, followed by an arkansas stone (group AS), appears to be an optimal treatment option.
Date Issued
2016-07
Publication Type
Article
Subject(s)
Subjects
dental implants
•
implant surface modification
•
implantoplasty
•
peri-implantitis
•
profilometry
•
resective peri-implantitis therapy
•
rotary instruments
Language(s)
en
Author(s)
Ramel, Christian F | |
Özcan, Mutlu | |
Jung, Ronald E | |
Hämmerle, Christoph H F | |
Thoma, Daniel S |
Journal
Clinical oral implants research
Publisher
Wiley-Blackwell
ISSN
0905-7161
Access(Rights)
restricted